低翹曲 B3M8 德國巴斯夫 PA6 耐高溫 可噴涂 高剛性 可加工 礦物填充40%Ultramid? B3M8 (8260)Polyamide 6BASF Corporation40% 礦物填料產(chǎn)品說明：Ultramid B3M8 (8260) is a 40% mineral reinforced PA6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low warp and resistance to sink-mark formation. It is also available in heat stabilized (Ultramid B3WM8) versions. It can be painted or chrome plated and is also available in pigmented versions.物性信息：基本信息填料/增強材料礦物填料, 40% 填料按重量特性尺寸穩(wěn)定性良好低翹曲性剛性，高可加工性，良好可噴涂的耐熱性，高機構評級EC 1907/2006 (REACH)RoHS 合規(guī)性RoHS 合規(guī)外觀可用顏色形式粒子加工方法注射成型物理性能干燥調節(jié)后的單位制測試方法比重1.49--g/cm3ASTM D792, ISO 1183收縮率 - 流動 (3.18 mm)0.90--%吸水率     24 hr1.1--%ASTM D570     23°C, 24 hr1.1--%ISO 62     飽和5.7--%ASTM D570     飽和, 23°C5.7--%ISO 62     平衡, 50% RH1.6--%ASTM D570     平衡, 23°C, 50% RH1.6--%ISO 62硬度干燥調節(jié)后的單位制測試方法洛氏硬度 (R 級)119--ASTM D785沖擊性能干燥調節(jié)后的單位制測試方法簡支梁缺口沖擊強度ISO 179     -30°C3.0--kJ/m2ISO 179     23°C3.0--kJ/m2ISO 179簡支梁無缺口沖擊強度 (23°C)120--kJ/m2ISO 179懸壁梁缺口沖擊強度 (23°C)53--J/mASTM D256熱性能干燥調節(jié)后的單位制測試方法熱變形溫度 (0.45 MPa, 未退火)195--°CISO 75-2/B熔融峰值溫度220--°CASTM D3418, ISO 3146線形熱膨脹系數(shù)     流動5.0E-5--cm/cm/°CASTM E831     流動4.6E-5--cm/cm/°C     橫向5.8E-5--cm/cm/°C電氣性能干燥調節(jié)后的單位制測試方法體積電阻率     1.50 mm> 1.0E+15--ohms·cmASTM D257     --> 1.0E+15--ohms·cmIEC 60093介電強度 1(1.50 mm)22--kV/mmASTM D149低翹曲 B3M8 德國巴斯夫 PA6 耐高溫 可噴涂 高剛性 可加工 礦物填充40%