高耐熱 TPU 德國巴斯夫 C90A 抗溶劑性 韌性好 水解穩(wěn)定 注塑 擠出成型Elastollan? C90AThermoplastic Polyurethane Elastomer (Polyester)BASF Corp. Thermoplastic Polyurethanes產(chǎn)品說明：Elastollan? C90A exhibits excellent abrasion resistance and toughness, good hydrolytic stability, good heat, oil, fuel and solvent resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan? C90A is supplied uncolored in pellet form.物性信息：基本信息特性抗溶劑性良好的撕裂強(qiáng)度良好耐磨損性耐熱性，高韌性良好水解穩(wěn)定外觀無色加工方法擠出注射成型物理性能額定值單位制測試方法比重1.21g/cm3ASTM D792熔流率（熔體流動速率） (210°C/21.6 kg)30 到 50g/10 minASTM D1238硬度額定值單位制測試方法肖氏硬度 (邵氏 A)90ASTM D2240機(jī)械性能額定值單位制測試方法拉伸模量 (注塑)39.3MPaASTM D412彎曲模量 (注塑)48.3MPaASTM D790泰伯耐磨性25.0mgASTM D1044Abrasion - DIN25mm3DIN 53516熱性能額定值單位制測試方法Softening Point - DMA113°C內(nèi)部方法彈性體額定值單位制測試方法拉伸應(yīng)力ASTM D412    ****應(yīng)變10.3MPaASTM D412    300%應(yīng)變22.8MPaASTM D412抗張強(qiáng)度44.1MPaASTM D412伸長率 (斷裂)520%ASTM D412撕裂強(qiáng)度 1133kN/mASTM D624壓縮yongjiu變形ASTM D395B    23°C, 22 hr25%ASTM D395B    70°C, 22 hr40%ASTM D395B熱性能額定值單位制測試方法玻璃轉(zhuǎn)化溫度-38.0°C內(nèi)部方法維卡軟化溫度128°CASTM D1525注射額定值單位制干燥溫度100 到 110°C干燥時(shí)間2.0 到 3.0hr建議的最大水分含量0.030%料筒后部溫度190 到 220°C料筒中部溫度190 到 220°C料筒前部溫度190 到 220°C射嘴溫度210 到 225°C擠出額定值單位制干燥溫度100 到 110°C干燥時(shí)間2.0 到 3.0hr料筒1區(qū)溫度170 到 210°C料筒3區(qū)溫度170 到 210°C料筒5區(qū)溫度170 到 210°C接頭溫度200 到 220°C口模溫度195 到 215°C高耐熱 TPU 德國巴斯夫 C90A 抗溶劑性 韌性好 水解穩(wěn)定 注塑 擠出成型高耐熱 TPU 德國巴斯夫 C90A 抗溶劑性 韌性好 水解穩(wěn)定 注塑 擠出成型